Now showing 1 - 3 of 3
  • Publication
    Evaluation of microwave plasma oxidation treatments for the fabrication of photoactive un-doped and carbon-doped TiO2 coatings
    The photoactivity of both un-doped and carbon-doped titanium dioxide (TiO2) coatings has been widely reported. In this paper, the use of a microwave plasma as a novel oxidation treatment for the fabrication of these coatings is evaluated. The photoactivity performance of the microwave plasma-formed coatings is benchmarked against those fabricated through air furnace oxidation as well as those deposited using reactive magnetron sputtering. The un-doped and carbon-doped TiO2 coatings were prepared respectively by microwave plasma-oxidizing titanium metal sheets and sputter deposited titanium carbide thin films. The resulting oxides were characterized using XPS, XRD, FEG-SEM, and optical profilometry. The oxide layer thicknesses achieved over the 15 to 45 minute oxidation times were in the range of 0.15 to 3.44 µm. These coatings were considerably thicker than those obtained by air furnace oxidation. The microwave plasma-formed oxides also exhibited significantly higher surface roughness values compared with the magnetron-sputtered coatings. The photoactivity performance of both un-doped and carbon-doped coatings was assessed using photocurrent density measurements. Comparing the un-doped TiO2 coatings, it was observed that those obtained using the microwave plasma oxidation route yielded photocurrent density measurements that were 4.3 times higher than the TiO2 coatings of the same thickness that were deposited by sputtering. The microwave plasma-oxidized titanium carbide coatings did not perform as well as the un-doped TiO2 probably due to the presence of un-oxidized carbide in the coatings, which reduced their photoactivity.
      1501Scopus© Citations 37
  • Publication
    Application of a novel microwave plasma treatment for the sintering of nickel oxide coatings for use in dye-sensitized solar cells
    In this study the use of microwave plasma sintering of nickel oxide (NiOx) particles for use as p-type photoelectrode coatings in dye-sensitized solar cells (DSSCs) is investigated. NiOx was chosen as the photocathode for this application due to its stability, wide band gap and p-type nature. For high light conversion efficiency DSSCs require a mesoporous structure exhibiting a high surface area. This can be achieved by sintering particles of NiOx onto a conductive substrate. In this study the use of both 2.45 GHz microwave plasma and conventional furnace sintering were compared for the sintering of the NiOx particles. Coatings 1 to 2.5 μm thick were obtained from the sintered particles (mean particle size of 50 nm) on 3 mm thick fluorine-doped tin oxide (FTO) coated glass substrates. Both the furnace and microwave plasma sintering treatments were carried out at ~ 450 °C over a 5 minute period. Dye sensitization was carried out using Erythrosin B and the UV-vis absorption spectra of the NiOx coatings were compared. A 44% increase in the level of dye adsorption was obtained for the microwave plasma sintered samples as compared to that obtained through furnace treatments. While the photovoltaic performance of the DSSC fabricated using the microwave plasma treated NiOx coatings exhibited a tenfold increase in the conversion efficiency in comparison to the furnace treated samples. This enhanced performance was associated with the difference in the mesoporous structure of the sintered NiOx coatings.
    Scopus© Citations 46  2511
  • Publication
    Conversion of amorphous TiO2 coatings into their crystalline form using a novel microwave plasma treatment
    Crystalline titanium dioxide (TiO2) coatings have been widely used in photo-electrochemical solar cell applications. In this study, TiO2 and carbon-doped TiO2 coatings were deposited onto unheated titanium and silicon wafer substrates using a DC closed-field magnetron sputtering system. The resultant coatings had an amorphous structure and a post-deposition heat treatment is required to convert this amorphous structure into the photoactive crystalline phase(s) of TiO2. This study investigates the use of a microwave plasma heat treatment as a means of achieving this crystalline conversion. The treatment involved placing the sputtered coatings into a 2.45 GHz microwave-induced nitrogen plasma where they were heated to approximately 550°C. It was observed that for treatment times as short as 1 minute, the 0.25-µm thick coatings were converted into the anatase crystalline phase of TiO2. The coatings were further transformed into the rutile crystalline phase after treatments at higher temperatures. The doping of TiO2 with carbon was found to result in a reduction in this phase transformation temperature, with higher level of doping (up to 5.8% in this study) leading to lower anatase-to-rutile transition temperature. The photoactivity performance of both doped and un-doped coatings heat-treated using both furnace and microwave plasma was compared. The carbon-doped TiO2 exhibited a 29% increase in photocurrent density compared to that observed for the un-doped coating. Comparing carbon-doped coatings heat-treated using the furnace and microwave plasma, it was observed that the latter yielded a 19% increase in photocurrent density. This enhanced performance may be correlated to the differences in the coatings’ surface morphology and band gap energy, both of which influence the coatings’ photoabsorption efficiency.
    Scopus© Citations 8  2512