    Growth mechanism of photoreduced silver nanostructures on periodically proton exchanged lithium niobate: Time and concentration dependence
    Photodeposition of metallic nanostructures onto ferroelectric surfaces, which have been chemically patterned using a proton exchange process, has recently been demonstrated. By varying the molar concentration of the AgNO3 solution and the illumination time, one can determine the initial nucleation sites, control the rate of nucleation and the height of silver nanostructures formed, and study the mechanisms by which these processes occurs. The nanoparticles are found to deposit preferentially in the boundary between ferroelectric and proton exchanged regions, in an area proton exchanged via lateral diffusion under the masking layer used for chemical patterning, consistent with our previous results. Using a short illumination time (3 min), we are able to determine that the initial nucleation of the silver nanostructure, having a width of 0.17±0.02µm and a height of 1.61±0.98nm, occurs near the edge of the reactive ion etched area within this lateral diffusion region. Over longer illumination times (15 min), we find that the silver deposition has spread to a width of 1.29±0.06µm, extending across the entire lateral diffusion region. We report that at a high molar concentration of AgNO3 (10¯² M), the amount of silver deposition for 5 min UV illumination is greater (2.88±0.58nm) compared to that at low (10¯4M) concentrations (0.78±0.35nm), however, this is not the case for longer time periods. With increasing illumination time (15 min), experiments at 10¯4 M had greater overall deposition, 6.90±1.52nm, compared to 4.50±0.76nm at 10 ¯² M. For longer exposure times (30min) at 10 ¯² M the nanostructure height is 4.72±0.59nm, suggesting a saturation in the nanostructure height. The results are discussed in terms of the electric double layer that forms at the crystal surface. There is an order of magnitude difference between the Debye lengths for 10¯² and 10¯4 M solutions, i.e., 3.04 vs. 30.40nm, which suggests the Debye length plays a role in the availability of Ag+ ions at the surface.
    Scopus© Citations 13  469
  • Publication
    Direct shape control of photoreduced nanostructures on proton exchanged ferroelectric templates
    Photoreduction on a periodically proton exchanged ferroelectric crystal leads to the formation of periodic metallic nanostructures on the surface. By varying the depth of the proton exchange (PE) from 0.59 to 3.10 µm in congruent lithium niobate crystals, the width of the lateral diffusion region formed by protons diffusing under the mask layer, can be controlled. The resulting deposition occurs in the PE region with the shallowest PE depth, and preferentially in the lateral diffusion region for greater PE depths. PE depth-control provides a route for the fabrication of complex metallic nanostructures with controlled dimensions on chemically patterned ferroelectric templates.
      436Scopus© Citations 9