Evaluation of the protective performance of hydrophobic coatings applied on carbon-fibre epoxy composites
Author(s)
Date Issued
2020-05-01
Date Available
2020-11-25T12:16:44Z
Abstract
Carbon-fibre epoxy composites are widely used for high performance structural applications, where they are often exposed to harsh environments. The result of moisture ingress has been extensively studied, causing significant deterioration in the mechanical properties of these composites. This study evaluates the performance of five commercial hydrophobic coatings as protective layers, to inhibit moisture ingress into the composite. The coatings evaluated were: NeverWet, HydroBead, SHC, Aculon and LiquidGlass. These coatings were characterised and compared in terms of hydrophobicity, surface energy, roughness and chemical composition. This study also evaluated two atmospheric plasma pre-treatments as a means of enhancing the adhesion performance of these coatings. The pre-treatments involved the use of an air plasma for the activation of the epoxy, as well as the plasma deposition of a nanometre thick SiOx interlayer coating. The durability and protective performance of the coatings, with and without the pre-treatments were then compared using an abrasion test as well as a water immersion study. The use of both plasma pre-treatments was found to enhance the adhesion and the abrasion performance of four out of the five coatings. Of the coatings and pre-treatments investigated, the LiquidGlass in conjunction with an SiOx coating interlayer was found to exhibit the highest abrasion resistance. This was followed by the composite which was plasma activated prior to the application of the Aculon coating. Only minor differences were observed when comparing the total moisture ingress (M%) of the epoxy, coated with the different hydrophobic layers. The composite coated with the Aculon and SiOx interlayer exhibited the least amount of moisture ingress, at 0.90 %, compared to 1.08 % of the uncoated specimen. The shear strength of epoxy composite, coated with the LiquidGlass, NeverWet and the activated Aculon combination, were within the range of the uncoated specimens, therefore the moisture ingress was reversible upon heating and no permanent damage to the epoxy-fibre interface was observed. It is concluded that, of the five coatings investigated, both the Aculon coating and LiquidGlass in combination with an SiOx interlayer coating, exhibit the greatest potential as protective layers for carbon fibre epoxy composites.
Sponsorship
European Commission - Seventh Framework Programme (FP7)
Science Foundation Ireland
Type of Material
Journal Article
Publisher
SAGE
Journal
Journal of Composite Materials
Volume
54
Issue
10
Start Page
1327
End Page
1338
Copyright (Published Version)
2020 SAGE
Language
English
Status of Item
Peer reviewed
This item is made available under a Creative Commons License
File(s)
No Thumbnail Available
Name
Evaluation of the protective performance of hydrophobic coatings applied on carbon-fibre epoxy composites .pdf
Size
753.97 KB
Format
Owning collection
Scopus© citations
7
Acquisition Date
Mar 28, 2024
Mar 28, 2024
Views
510
Acquisition Date
Mar 28, 2024
Mar 28, 2024
Downloads
375
Last Week
9
9
Last Month
36
36
Acquisition Date
Mar 28, 2024
Mar 28, 2024