Serendipity following attempts to prepare C-doped rutile TiO2

Files in This Item:
File Description SizeFormat 
accepted_paper_for_upload.pdf1.03 MBAdobe PDFDownload
Title: Serendipity following attempts to prepare C-doped rutile TiO2
Authors: Neville, Elaine M.
Ziegler, Julia
MacElroy, J. M. Don
Thampi, Ravindranathan
Sullivan, James A.
Permanent link: http://hdl.handle.net/10197/5186
Date: 30-Jan-2014
Abstract: Attempts to mimic the band gap narrowing seen in anatase TiO2 following C-doping of the lattice where the C arose from a melamine borate precursor were made in situations where the sol-gel mixture was directed towards rutile formation. The formed materials were characterised using XRD, BET, UV-Vis spectroscopy, XPS and TEM and their activities in promoting the photo-degradation of 4-chlorophenol were analysed. It was found that carbon was not doped into the lattice (in contrast to the situations where the sol-gel mixture was directed towards the precipitation of anatase TiO2). In spite of how common reports of the preparation of C-doped TiO2 using sol-gel processes have been, the presence of carbon dopant precursors in a crystallising sol does not necessarily result in the incorporation of C dopants within the final crystalline material, i.e. the nature of the condensing sol is also important. The presence of melamine borate did however increase the proportion of rutile in the final mixture (indeed in the presence of melamine borate the pure rutile phase was formed) and also resulted in materials with higher surface areas (as measured using BET). Furthermore, TEM has shown that rutile TiO2 condensed in the presence of melamine borate had a much more distinct rod-like shape than that condensed in its absence (the latter being more spherical in shape). These materials, notwithstanding the absence of any dopant effect, demonstrated enhanced photocatalytic activity when compared with analogous materials prepared in the absence of melamine borate and this effect is ascribed to both their relatively larger surface areas and their specific shape. Therefore, we have serendipitously come across a method for improving the performance of rutile photocatalysts while searching for a method to generate C-doped rutile TiO2.
Funding Details: Science Foundation Ireland
Type of material: Journal Article
Publisher: Elsevier
Copyright (published version): 2014 Elsevier
Keywords: Photocatalysts;Doping;Rutile TiO2
DOI: 10.1016/j.apcata.2013.11.024
Language: en
Status of Item: Peer reviewed
Appears in Collections:Chemistry Research Collection

Show full item record

SCOPUSTM   
Citations 50

6
Last Week
0
Last month
checked on Jun 23, 2018

Google ScholarTM

Check

Altmetric


This item is available under the Attribution-NonCommercial-NoDerivs 3.0 Ireland. No item may be reproduced for commercial purposes. For other possible restrictions on use please refer to the publisher's URL where this is made available, or to notes contained in the item itself. Other terms may apply.